BSC紫外,可见及,近红外宽频混合立体分束镜

Absorption

<24%

Coating

<1% reflectance (entrance and exit faces)

Edge Dimensions

A±0.3 mm

Material

UV-grade synthetic fused silica

Surface Flatness

λ/4 per clear aperture at 632.8 nm

Surface Quality

40-20 scratch and dig, beveled edges

Transmission

43%±6% for 280–400 nm wavelength range;
38%±6% for 250–280 nm wavelength range;
s- and p-components matched to within 5% for both ranges

Transmitted Beam Deviation

<10 arc minutes

BSC-250-400-050

03 BSC 055

11.4 × 11.4

12.7

250–400

BSC-250-400-100

03 BSC 057

22.9 × 22.9

25.4

250–400

Absorption

<10%

Clear Aperture

90% of central area

Coating

HEBBAR? antireflection coating (entrance and exit faces)

Edge Dimensions

A±0.3 mm

Material

N-BK7

Surface Flatness

λ/2 per clear aperture at 632.8 nm

Surface Quality

60-40 scratch and dig, beveled edges

Transmission

45%±6%

Transmitted Beam Deviation

<10 arc minutes

BSC-450-700-040

03 BSC 003

9.0 × 9.0

10.0

450–700

BSC-450-700-050

03 BSC 005

11.4 × 11.4

12.7

450–700

BSC-450-700-080

03 BSC 007

18.0 × 18.0

20.0

450–700

BSC-450-700-100

03 BSC 009

22.9 × 22.9

25.4

450–700

BSC-450-700-200

03 BSC 015

45.7 × 45.7

50.8

450–700

Absorption

<10%

Clear Aperture

90% of central area

Coating

HEBBAR? antireflection coating (entrance and exit faces)

Edge Dimensions

A±0.3 mm

Material

N-BK7

Surface Flatness

λ/2 per clear aperture at 632.8 nm

Surface Quality

60-40 scratch and dig, beveled edges

Transmission

45%±6%

Transmitted Beam Deviation

<10 arc minutes

BSC-700-1000-050

03 BSC 026

11.4 × 11.4

12.7

700–1000

BSC-700-1000-100

03 BSC 029

22.9 × 22.9

25.4

700–1000