制造标准：95/28/EG; V等
特点与用途：
产品名称：熔融滴落试验仪
依据标准: 95/28/EG; V
简要描述：汽车内部设备用材料燃烧性能测定。将试样水平放在格栅式试品架上，利用500W电热器对其辐射加热，观察融化的试样滴落物落到下面的收集盘上后，与收集盘中的棉花接触后是否燃烧，以及棉花是否燃烧，从而判断材料的可燃性。
设备配置:500W电热器、格式试品台、滴落物收集盘、试验支架、放大器、校准设备。
熔融滴落试验仪应用于汽车内部设备所用材料的燃烧性能的测定。将试样水平放在格栅式试品架上，利用500W电热器对其辐射加热，观察融化的试样滴落物落到下面的收集盘上后，与收集盘中的棉花接触后是否燃烧，以及棉花是否燃烧，从而判断材料的可燃性。
WAZAU的熔融滴落试验仪参考标准95/28/EG
Combustionbehavior of materials in compliance with the European Guideline
Appendix V95/28/EG
1.Principle
A sampleis placed in a horizontal position and exposed to an electrical heater. Underthe sample there is a box to collect drops.
Inside thebox there is some cotton to detect if the drops are burning.
Theheating source is a heater having a power of 500 Watts. The area exposed toradiation consists of a transparent Quartz plate of an diameter of 100 mm
2.Calibration
A heatingflux measuring device （radiometer） of the Gardon foilte with a measuring range of at least 10 W/ cm2 is used for calibration.
Thecalibration of the heating flux measuring device has to be calibrated by areference heating flux measuring device everytime the heater has to becalibrated. The reference heating flux measuring device has to be re-calibratedaccording a national standard.
3.Calibrationcheck
Theradiation density caused by the the energy impact, which has according to thecalibration a radiation density of 3 W/cm2, has to be controlled often. Atleast once every 50 hours of operation. The device has to be calibrated againif the measured values have changed more than
0.06W/cm2.
4.Procedureof calibration
The devicehas to be placed at a draught safe spot. The air velocity must not higher than0.2 m/s. The heating flux device has to be inserted into the test rig insteadof the sample. The black plate of the heating flux device must be located inthe middle of the heater.
Then thepower is turn on using the potentiometer POWER REGULATOR until the radiationdensity is 3 W/cm2 in the center of the heater surface. After the potentiometerwas adjusted to provide the value 3 W/cm2 the potentiometer should not bere-adjusted for 5 minutes to stabilize it.
5.Sample
The samplemust have the dimensions 70 mm x 70 mm.
Ifpossible the samples should be production as the ready product. If the productis thicker than 13 mm its thickness has to be reduced to 13 mm at the sideopposite to the side seen by the pengers. If this is not possible the testmust be conducted in compliance with a Technical Service with the sample havingthe regular thickness. This, however, must be stated in the report. Compositematerials are to be tested as homogeneous materials.
In case ofmaterials consisting of different layers, not clified as componentmaterials, all layers of a thickness up to 13 mm have to be tested on the sideexposed to the interieur of a vehicle. The total m of the sample must be atleast 2 g. If the m is below that a sufficient number of samples have to beadded.
If bothsides of the sample are different, each side has to be testesd, resulting in atest of eight samples.
Before thetest the samples and the cotton have to be conditioned at a temperature of 23 ℃
6. Doingthe calibration
1） Remove thesample holder.
2） Mount thecalibration ring.
3） Connect thesensor to te amplifier.
4） Regulate theenergy using the POWER REGULATOR potentiometer.